Red Phosphorus Flame Retardant Master Batch FRP-302Y
I. Product Instruction
FRP-302Y is a red phosphorus flame retardant with a high-performance cost ratio, formed by super-fine pulverization of raw red phosphorus and then secondary coating on the surface by in-situ polymerization through inorganic flame retardant and melamine formaldehyde resin.
Special use for PA with low dosage which can save more cost.
II. Product Technical Data Sheet
Item | Unit | Value |
The effective of flame retardancy | % | ≥50 |
Appearance | Master batch (red/black color) | |
Carrier | Import new compatilizer | |
Density | g/cm3 | 1.4-1.6 |
Content of water | % | ≤0.5 |
Kindle temperature | ℃ | ≥360 |
Melting temperature | ℃ | 140 |
Additives amount | % | 12-14 |
Properties | UL94-V0 (T2.0mm) |
III. Product Features
1. High efficiency, with small adding will achieve high flame retardancy.
2. Good mechanical property.
3. New carrier, with new compatilizer as the carrier, it’s our exclusive technology in China.
4. Eco-friendly, non-halogen, achieve SGS and RoHS requirements.
5. Better flow ability.
6. Low moisture absorption.
7. Easy handling.
8. Low cost.
IV. Application
PA6/66, PE, PET, HIPS, TPU, PPO, PC, Silastic.
V. Package Storage and Transportation
1. Paper plastic compound bag, 25kg/bag.
2. Transport as non-dangerous chemical product.
3. Storage in cool dry place.
Examples
Formular | PA6 | FRP-302Y | Glass Fiber |
Proportion | 54% | 16% | 30% |
Processing Temperature | 300℃ | ||
Properties | UL94-V0 (T2.0mm) |
Note: Addition in the table is suggested. The suitable addition should be checked by test.
Red Phosphorus Flame Retardant Master Batch FRP-302Y
I. Product Instruction
FRP-302Y is a red phosphorus flame retardant with a high-performance cost ratio, formed by super-fine pulverization of raw red phosphorus and then secondary coating on the surface by in-situ polymerization through inorganic flame retardant and melamine formaldehyde resin.
Special use for PA with low dosage which can save more cost.
II. Product Technical Data Sheet
Item | Unit | Value |
The effective of flame retardancy | % | ≥50 |
Appearance | Master batch (red/black color) | |
Carrier | Import new compatilizer | |
Density | g/cm3 | 1.4-1.6 |
Content of water | % | ≤0.5 |
Kindle temperature | ℃ | ≥360 |
Melting temperature | ℃ | 140 |
Additives amount | % | 12-14 |
Properties | UL94-V0 (T2.0mm) |
III. Product Features
1. High efficiency, with small adding will achieve high flame retardancy.
2. Good mechanical property.
3. New carrier, with new compatilizer as the carrier, it’s our exclusive technology in China.
4. Eco-friendly, non-halogen, achieve SGS and RoHS requirements.
5. Better flow ability.
6. Low moisture absorption.
7. Easy handling.
8. Low cost.
IV. Application
PA6/66, PE, PET, HIPS, TPU, PPO, PC, Silastic.
V. Package Storage and Transportation
1. Paper plastic compound bag, 25kg/bag.
2. Transport as non-dangerous chemical product.
3. Storage in cool dry place.
Examples
Formular | PA6 | FRP-302Y | Glass Fiber |
Proportion | 54% | 16% | 30% |
Processing Temperature | 300℃ | ||
Properties | UL94-V0 (T2.0mm) |
Note: Addition in the table is suggested. The suitable addition should be checked by test.